STAINLESS STEEL 310/310S

STAINLESS STEEL 310/310S

ASTM A 240, A 276, A 312 
UNS S31000 / UNS S31008
DIN 1.4845

 

What forms of 310/310S Stainless Steel are available at Haohua Industry?

Sheet
Plate
Bar
Pipe & Tube
Fittings (i.e. flanges, slip-ons, blinds, weld-necks, lapjoints, long welding necks, socket welds, elbows, tees, stub-ends, returns, caps, crosses, reducers, and pipe nipples)
Weld Wire
 

310/310S Stainless Steel Overview310 Stainless Plate

Stainless steel 310/310S is an austenitic heat resistant alloy with excellent resistance to oxidation under mildly cyclic conditions through 2000ºF. Its high chromium and nickel contents provide comparable corrosion resistance, superior resistance to oxidation and the retention of a larger fraction of room temperature strength than the common austenitic alloys like Type 304. Stainless 310 is often used at cryogenic temperatures, with excellent toughness to -450°F, and low magnetic permeability.

**As you can see below, Grade 310S is a low carbon version of grade 310. 310S is less prone to embrittlement and sensitization in service.

 

310 UNS S31000 Chemical Composition, %

Cr

Ni

C

Si

Mn

24.0-26.0

19.2-22.0

.25 Max

1.50 Max

2.00 Max

P

S

Mo

Cu

Fe

.045 Max

.03 Max

.75 Max

.50 Max

Balance

 

310S UNS S31008 Chemical Composition, %

Cr

Ni

C

Si

Mn

24.0-26.0

19.2-22.0

.08 Max

1.50 Max

2.00 Max

P

S

Mo

Cu

Fe

.045 Max

.03 Max

.75 Max

.50 Max

Balance

 

What are the characteristics of 310/310S Stainless?

Oxidation resistance to 2000°F
Moderate strength at high temperature
Resistance to hot corrosion
Strength and toughness at cryogenic temperatures 
 

Typical Applications for 310/310S Stainless

Kilns
Heat Exchangers
Radiant Tubes
Muffles, retorts, annealing covers
Tube hangers for petroleum refiing adn steam boilers
Coal gasifier internal components
Saggers
Furnace parts, conveyor belts, rollers, oven linings, fans
Food processing equipment
Cryogenic structures 
 

Fabrication with Stainless 310/310S

Type 310/310S is readily fabricated by standard commercial procedures. In comparison to carbon steel, stainless steels are tougher and tend to work harden rapidly.

Type 310/310S can be welded using all of the common welding processes.

 

Mechanical Properties
Representative Tensile Properties


Temperature, °F

Ultimate Tensile Strength, ksi

.2% Yield Strength, ksi

Elongation Percent

70

80.0

35.0

52

1000

67.8

20.8

47

1200

54.1

20.7

43

1400

35.1

19.3

46

1600

19.1

12.2

48

 

Typical Creep-Rupture Properties


Temperature, °F

Minimum Creep 0.0001%/hr, ksi

100,000 Hour Rupture Strength, ksi

12000

14.9

14.4

1400

3.3

4.5

1600

1.1

1.5

1800

.28

.66

*Note: The specifications noted including ASTM, ASME, or other applicable authorities are correct at the time of publication. Other specifications may apply for use of these materials in different applications.